The aim of this study is to introduce a new qualification approach designed to enhance the overall integrity of complex cooling structures in gas turbine blades produced through 3D printing, with a focus on achieving maximum density. The primary objective is to present a comprehensive qualification and validation methodology tailored for components manufactured via binder jetting printing and powder-based atomic diffusion additive manufacturing. This innovative qualification approach undergoes validation through stages encompassing design, printing, comprehension of thermal debinding and sintering processes, post-processing, optimization, and characterization, all aimed at achieving complex cooling structures with optimal density using stainless steel material and In718 as a case study. Subsequently, the material properties obtained are compared with those of IN718 produced via laser-based manufacturing. Thorough characterization is conducted before and after sintering to assess the impact of sintering on density enhancement. Experimental optimization employing the Taguchi matrix with an L9 orthogonal array involves the selection of three key parameters: sintering time, sintering temperature, and heat treatment. The procedural framework established in this research is applicable to high-temperature applications wherein components are fabricated using atomic diffusion additive manufacturing or binder jetting printing techniques. Testing and inspection procedures involve neutron scattering, radiography, and CT scanning methods, with a specific emphasis on neutron scattering measurements conducted under externally heated and internally cooled conditions to evaluate residual strains within the gas turbine environment. Understanding the interplay between residual stresses originating from manufacturing processes and thermal stresses provides valuable insights into the impact of additive manufacturing on component performance in thermal environments, thus contributing to the advancement of the proposed study.
Jayanta Kapat, Committee Chair.
Read More